Wiper Blade
Automotive wiper blade grades combining low friction and haze-free water repellency, with a service life of over 300,000 cycles.
Key Benefits
- High water repellency without haze
- Excellent low friction
- Long life of over 300,000 cycles
- Wide service temperature
Applications
- Windshield wiper blade
- Low-friction parts
Typical Properties by Grade (per Catalog)2 grades
| Grade | Application | Product | Appearance | Specific Gravity | Williams Plasticity | Organic Peroxide | Linear Shrinkage (%) | Curing Condition | Mechanical PropertiesKS M6518 | Compression Set (%)180℃/22hr | Heat Resistance250℃/72hr | Oil ResistanceIRM903 Oil, 150℃/72hr | Volume Resistivity (Ω·cm) | Reference | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Trade Name | PHR | Press Cure℃/min | Post Cure℃/hr | HardnessShore A | Tensile Strengthkgf/cm² | Elongation at Break% | Tear Strengthkgf/cm · Type B | Hardness Δ | Tensile Δ% | Elongation Δ% | Hardness Δ | Tensile Δ% | Elongation Δ% | Volume Δ% | ||||||||||
| 자동차 Wiper Blade 용 | Low friction, Wiper blade parts | TS 1265U | Milky-White 유백색 | 1.21 | 220 | SC-8B | 1.2 | 3.3 | 170/10 | 200/4 | 65 | 75 | 300 | 25 | 20 | – | – | – | – | – | – | – | – | – |
| 자동차 Wiper Blade 용 | Low friction, Wiper blade parts | TS 1271U | Milky-White 유백색 | 1.22 | 240 | SC-8B | 1.2 | 3.2 | 170/10 | 200/4 | 70 | 72 | 280 | 25 | 19 | – | – | – | – | – | – | – | – | – |
← Swipe the table sideways →
Same layout as the product catalog (Apr 2026). Values are typical measurements based on KS M6518, not specifications, and may vary with curing agent and cure conditions.
TS 1265U Properties
| Properties | Standard | TS 1265U |
|---|---|---|
| Appearance | - | Dark gray |
| Williams Plasticity | mm/100 | 220 |
| Specific gravity | - | 1.21 |
| Hardness | Shore A | 65 |
| Tensile Strength | kgf/cm² | 71 |
| Elongation at break | % | 240 |
| Tear strength | kgf/cm | 23 |
← Swipe the table sideways →
Properties obtained using 1.2 part of SC-8B(50P)(2,5-bis(tert-butylperoxy)-2,5-dimethyl hexane) on 2mm thick slabs: molded 10 minutes at 170℃ and post-cured 4 hours at 200℃.
Product Photo
Wiper Blade
Technical Data Downloads
TDS files are in English; MSDS (Material Safety Data Sheets) are Korean PDFs. Please contact us for grades without an MSDS.